Negative electrode formulation for high-temperature performance of lead-acid batteries (containing the first hydrogen evolution inhibitor Bi2O2CO3 and the second hydrogen evolution inhibitor ZnO).

The basic formula of the negative electrode (number of weight) is: 100 parts lead powder, 8 ~ 11 parts dilute sulfuric acid, 9 ~ 13 parts deionized water, 0.06 ~ 0.14 parts short fiber, 0.10 ~ 0.20 parts lignin, 0.3 ~ 0.45 parts humic acid, synthetic tanning agent (NF type, α naphthalene sulfonate formaldehyde polymer), 0.05 ~ 0.1 parts barium sulfate, 0.8 ~ 1.2 parts Carbon black 0.10 ~ 0.15, high conductivity graphite 0.04 ~ 0.08.

Hydrogen evolution inhibitor and humic acid mixed into the negative plate can inhibit the hydrogen evolution of the negative electrode, reduce the water loss rate, and extend the high-temperature cycle life of the battery.

The preparation process of the negative lead paste is as follows: Bi2O2CO3, ZnO, and humic acid are mechanically mixed, and the mixture is evenly stirred. Dry mix it with lignin, synthetic tanning agent, short fiber, barium sulfate, carbon black, high conductivity graphite, etc. Add lead powder and stir for 5to 10 minutes to stir well; After stirring for 1 minute, add deionized water within 2 minutes and stir evenly, add dilute sulfuric acid within 3 minutes and stir for 10 to 15 minutes to make a negative lead paste.

Test data:

แบตเตอรี่ที่ประกอบและแบตเตอรี่ธรรมดาได้รับการทดสอบสำหรับการชาร์จแบบลอยตัวแบบเร่งที่อุณหภูมิสูง: ทดสอบ 3 ชั่วโมงก่อน และหลังจากชาร์จเต็มแล้ว แบตเตอรี่จะถูกชาร์จในสภาพแวดล้อม 60°C เป็นเวลา 30 วัน และหลังจากถอดออกแล้ว แบตเตอรี่จะถูกปล่อยทิ้งไว้เป็นเวลา 24 ชั่วโมง . ทดสอบ 3 ชม. ในสภาพแวดล้อม 25°C และชาร์จใหม่เป็นรอบจนกว่าความจุ 3 ชม. ของแบตเตอรี่จะต่ำกว่า 80%